Optical gain of vertically coupled Cd0.6Zn0.4Te/ZnTe quantum dots

Journal article

The optical modal gain of Cd_0.6Zn_0.4Te/ZnTe double quantum dots was measured using a variable stripe length method, where large and small quantum dots are separated with a ZnTe layer. With a large (~18 nm) separation layer thickness of ZnTe, two gain spectra were observed, which correspond to the confined exciton levels of the large and small quantum dots, respectively. With a small (~6 nm) separation layer thickness of ZnTe, a merged single gain spectrum was observed. This can be attributed to a coupled state between large and small quantum dots. Because the density of large quantum dots (4 × 10¹⁰ cm⁻²) is twice the density of small quantum dots (2 × 10¹⁰ cm⁻²), the density of the coupled quantum dots is determined by that of small quantum dots. As a result, we found that the peak gain (123.9 ± 9.2 cm⁻¹) with the 6 nm separation layer is comparable to that (125.2 ± 29.2 cm⁻¹) of the small quantum dots with the 18 nm separation layer.

Authors: Mei, M; Kim, M; Kim, M; Kim, I; Lee, HS

• Publication status: Published
• Peer review status: Peer reviewed
• Publisher: MDPI
• Journal: Nanomaterials
• Volume: 13
• Issue: 4
• Article number: 716
• Publication date: 2023-02-13
• Acceptance date: 2023-02-10
• DOI: 10.3390/nano13040716
• EISSN: 2079-4991
• Language: English
• Keywords: CdZnTe; amplified spontaneous emission; exciton; optical modal gain; FFR; quantum dots